Plywood Material For Cabinet/Kitchen 6063 CQC Manufacture Aluminum
Profile
Product Description ♦
Packing : Protect film for each profile, shrink film / kraft paper
exterior for each bundle or pack as customer request.
FOB port: Foshan, Shenzhen, Guangzhou
Delivery time: 15-20 days after receiving the deposite.
Payment term: 30% deposite and 70% balance after the delivery
Material: 6063 Alloy
Temper: T5
Brand name: Kaiyamei Aluminum
Finish: Mill Finished, Anodizing, Electrophoresis, Powder Coating
,Polish, Wood grain, Sand Blasting
Color: Clear Satin, Bronze, Black, Golden, Silver,
Thickness: 0.8mm - 1.5mm
MOQ: 500KG. Usually 12 tons for a 20 feet container; 24 tons for a
40 feet container.
Length: 5.8-5.98m, or as customer's request
Sample delivery: Two weeks (one week for mould +one week making
sample)
Sample design: It is better we can get your drawing or sample, we
mainly make according to your design, and we can keep confidential
for your design.
Maximum extruder machine: 8000 tons; Minimum extruder machine: 500
ton
If the profiles are customized, we will make the sample first,
after we get the confirmation from you, we will start production.
Our profiles advantages:
(1) Complex integral shapes
(2) Cost effective
(3) Low tooling costs
(4) Design flexibility
(5) Versatility in joining
(6) Machinable
(7) Rapid prototyping
(8) Short delivery
(9) Wide range of finishes
(10) Plenty of patterns and colors for your choice.
(11) Strict control for surface finish, very little scratch.
(12) Accurate mold as well as accurate size.
(13) Standard alloy composition
(14) Both ends of the profiles are very plain and with no burr.
Surface treatment ♦
Anodized surface treatment
Anodized surface treatment: minimum partial thickness of coating on
decorative surface around 8μm - 10μm.
|
Powder coating surface treatment
Powder coating surface treatment: minimum partial thickness of
coating on decorative surface≥40μm;Maximum partial thickness≤120μm.
|
General Chemical Composition of Alloy
| Alloy | 6063(%) | 6061(%) | 6082(%) |
| Silicon Si | 0.20~0.60 | 0.40~0.80 | 0.7~1.2 |
| Iron Fe | 0.35 | 0.70 | 0.5 |
| Copper Cu | 0.10 | 0.15~0.40 | 0.1 |
| Manganese Mn | 0.10 | 0.15 | 0.4~0.8 |
| Manganese Mg | 0.45~0.90 | 0.18~1.2 | 0.6~0.8 |
| Chromium Cr | 0.10 | 0.04~0.35 | 0.25 |
| Zine Zn | 0.10 | 0.25 | 0.2 |
| Titanium Ti | 0.10 | 0.15 | 0.1 |
| Others(each) | 0.05 | 0.05 | 0.05 |
| Others | 0.15 | 0.15 | 0.15 |
| Aluminum | Remainder | Remainder | Remainder |
Mechanical Properties of Sections under Room Temperature
Alloy |
State | Tensile strength test | Hardness test |
| Tensile strength Rm M pa | Non-proportional Stretching Stress | Stretching rate | Pattern thickness | HV | HW |
| Rp0.2Mpa | (A50mm%) | mm | HV | HW |
|
| 6063 | T4 | 130 | 75 | 14 | - |
| T5 | 160 | 110 | 8 | 0.8 | 58 | 8 |
| T6 | 205 | 180 | 8 | - |
6061 | T4 | 184 | 110 | 16 | - |
| T6 | 265 | 245 | 8 | - |
6082 (6351) | T4 | 205 | 110 | 12 | - |
| T6 | 290 | 250 | 6 | - |
About us :
Foshan Kaiya Aluminum Co., Ltd is a comprehensive and professional
enterprise integrating research, design production and sales of
aluminium extrusion profiles for construction and industrial
applications. There are currently 24 aluminum extrusion process
lines at 500MT TO 2500MT, 5 process lines for anodizing, 3 process
lines for powder coating, 2 process line for painting, 2process
line of polishing and brushing. We still have 2 packing line. Our
annual production capacity has reached 80,000 tons which is at the
forefront of the aluminium industry in China.